Исследование свойств клееной фанеры на основе термомодифицированного березового шпона

Abstract

The article presents the results of a study of the physical and mechanical properties of glued plywood based on thermomodified birch veneer. The implementation of a full-factor experiment in the temperature range from 160 to 200 С with a duration of 120 to 240 minutes made it possible to establish the nature of the dependence of the change in strength during static bending and strength when chipping along the adhesive layer on the heat treatment mode of the veneer. Plywood based on thermomodified veneer cquires higher strength and water resistance, which makes it possible to significantly expand the scope of application of glued wood based on carbamide-formaldehyde resins.

Приведены результаты исследования физико-механических свойств клееной фанеры на основе термомодифицированного березового шпона. Реализация полнофакторного эксперимента в диапазоне температур от 160 до 200 С продолжительностью от 120 до 240 мин позволила установить характер зависимости изменения прочности при статическом изгибе и прочности при скалывании по клеевому слою от режима термообработки шпона. Фанера на основе термомодифицированного шпона приобретает более высокие показатели прочности и водостойкости, что позволяет значительно расширить область применения клееной древесины на основе карбамидоформальдегидных смол.