Методика испытаний на коррозионно-механическое изнашивание образцов быстрорежущей стали для дереворежущего инструмента с вакуумно-плазменными покрытиями

Abstract

A tеhnique for testing sаmples of high-speed steel with vacuum-plasma coatings for corrosion-mechanical wear in the environment of products of dry thermal destruction of wood has been developed. The technique is based on measuring the diagonals of prints obtained on the surface of samples using a pyramidal indenter. Diagonals of prints are reduced as a result of abrasive mechanical action in the presence of wood pyrolysis products. As a body abrading samples, a taffeta disk is used. The speed of the relative movement of the test specimens and the disc, as well as the forces of their clamping, are determined on the basis of the requirement for simulating the cutting regime. Products of dry thermal destruction of hardwood and coniferous wood were obtained and their chemical composition was determined.

Разработана методика испытаний образцов быстрорежущей стали с вакуумно-плазменными покрытиями на коррозионно-механическое изнашивание в среде продуктов сухой термодеструкции древесины. Методика основана на измерении диагоналей отпечатков, полученных на поверхности образцов с помощью пирамидального индентора. Диагонали отпечатков уменьшаются в результате истирающего механического воздействия в присутствии продуктов пиролиза древесины. В качестве тела, истирающего образцы, используется диск из тафты. Скорость относительного движения испытываемых образцов и диска, а также усилия их прижима назначаются исходя из требования имитации режима резания. Получены продукты сухой термодеструкции древесины лиственных и хвойных пород и определeн их химический состaв.