Результаты испытаний на коррозионно-механическое изнашивание образцов быстрорежущей стали для дереворежущего инструмента с вакуумно-плазменными покрытиями

Abstract

Testing of high-speed steel specimens with vacuum-plasma coatings for mechanical and chemical wear was carried out. It has been established that the mechanical action on samples of high-speed steel without coatings in conditions of the presence of products of dry thermal destruction of wood increases the wear rate of the samples to 50 % in comparison with wear outside the pyrolysis products. It has been found that the multicomponent nanostructured coatings obtained under bombardment with a stream of low-energy gas ions increase the corrosion-mechanica resistance of samples in products of dry thermal destruction of wood from 4 to 10 times in comparison with uncoated samples.

Проведены испытания образцов быстрорежущей стали с вакуумно-плазменными покрытиями на механо-химическое изнашивание. Установлено, что механическое воздействие на образцы быстрорежущей стали без покрытий в условиях присутствия продуктов сухой термодеструкции древесины увеличивает интенсивность изнашивания образцов до 50 % по сравнению с изнашиванием вне среды продуктов пиролиза установлено, что исследованные многокомпонентные наноструктурные покрытия, полученные в условиях бомбардировки потоком низкоэнергетичных ионов газов, повышают коррозионно-механическую стойкость образцов в продуктах сухой термодеструкции древесины от 4 до 10 раз по сравнению с образцами без покрытий.