Влияние промежуточного слоя NI-УДА на адгезию покрытия ZrN-Ni-УДА твердосплавных ножей дереворежущего инструмента

Abstract

In this work, combined Z rC-Ni-ultradisperse diamonds (UDD) coatings were synthesized on hard alloy knive blades by electroplating and cathode arc evaporation PVD techniques. The morphology of ZrC-coating was characterized for the PVD. The average roughness value Ra of the upper ZrC-coating layer of ZrС-Ni-UDD-coating was 0,27 ± 0,09 μm. The obtained high values of the critical loads on the scratch track of the ZrC-Ni-UDD coating in 24 N prove a sufficiently high value of the adhesion strength of the intermediate Ni-UDA layer with hard alloy WC-Co substrate. It was contributed to an increase of durability period of modified cutting tools to be 1,5–1,6 times higher, if compared with bare tools, when milling laminated chipboard during held pilot tests.

В данной работе комбинированные ZrC-Ni-ультрадисперсные алмазные (УДА) покрытия были синтезированы на твердосплавные лезвия ножей методами электроосаждения и КИБ. Морфология ZrC-покрытия была характерной для КИБ метода. Cреднее значение шероховатости Ra верхнего ZrC-слоя ZrС-Ni-УДА- покрытия составляло 0,27 ± 0,09 мкм. Полученные высокие значения критических нагрузок 24 Н на скретч-треках ZrС-Ni-УДА-покрытия подтвердили достаточно высокое значение адгезии промежуточного Ni-УДА слоя с твердосплавной WC-Co основой. Это способствовало увеличению периода стойкости модифицированного инструмента при резании ламинированных древесно-стружечных плит в 1,5–1,6 раза по сравнению с инструментом без покрытий во время проведения опытно-промышленных испытаний.