Модификация дереворежущего инструмента с твердосплавными ножами Ni-УДА/MoN-покрытием

Abstract

In this work, the mechanical properties (the microhardeness, the adhesion strength) of two layers Ni-ultradisperse diamonds (UDD)/MoN-coatings on hard alloys of the tungsten carbide WC – 2 wt. % Co knives of a wood-cutting milling tool have studied. MoN-coatings were deposited by cathode arc evaporation physical vapor deposition (CAE-PVD) technique on hard alloys knives. The Ni-UDD layer was a composite nanodia-mond-containing chemi-cal coating (CChC) to improve tool life. The obtained value of the critical loads on the scratch track of the coating in 40 N proves a high value of the adhesion strength of the Ni-UDD/MoN-coating with hard alloy WC-Co substrate. Due to their high mechanical features Ni-UDD/MoN-coatings can be used to increase the durability period of a wood-cutting milling tool when cutting chipboards by CNC machines.

В данной работе исследованы механические свойства (микротвердость, адгезия) двухслойных (УДА)/MoN-покрытий с Ni-ультрадисперсными алмазамина твердосплавных (карбид вольфрама WC – 2 вес. % Co) ножах дереворежущего фрезерного инструмента. MoN-покрытия осаждались методом конденсации вещества из плазменной фазы в вакууме с ионной бомбардировкой (КИБ) на твердосплавные ножи. Ni-УДА слой являлся композиционным содержащим наноалмазы химическим покрытием (КХП), осажденным на образцы с MoN-покрытием с целью увеличения ресурса работы инструмента. Полученное значение критических нагрузок в 40 Н на скретч-треке покрытия свидетельствует о высокой величине адгезии Ni-УДА/MoN-покрытия с подложкой из твердого сплава WC-Co. Благодаря своим высоким механическим свойствам Ni-УДА/MoN-покрытия могут использоваться для увеличения периода стойкости дереворежущего фрезерного инструмента при резании древесно-стружечных плит на станках с ЧПУ.