Нижняя граница температуры начала формирования α-мартенсита охлаждения в сплавах на основе железа

Abstract

The concept of the leading role of the subsystem of 3d electrons in changing the stability of the γ(fcc) and α (bcc) phases is used to conclude that the stability of the α phase having a smaller thermal expansion coefficient β increases as the temperature decreases. It is suggested to find the smallest possible temperature Ms(min) of the onset of spontaneous γ-α martensite transformation in iron-based alloys from the condition of the equality between the volume of the γ-phase unit cell and the quantity specified by the effective atomic radii of alloy components given in the generalized Periodic Table. The calculated Ms(min) values are shown to agree with the experimental data for pure iron and Fe-Ni and Fe-C alloys.

На основе представлений о ведущей роли подсистемы Зd-электронов в изменении стабильности γ (ГЦК)- и α (ОЦК)-фаз делается вывод об увеличении стабильности α-фазы (в ходе понижения температуры), обладающей меньшим коэффициентом теплового расширения β. Наименьшее возможное значение температуры начала спонтанного γ-α-мартенситного превращения Ms(min) в сплавах на основе железа предлагается находить из условия равенства объема элементарной ячейки γ-фазы значению, задаваемому эффективными радиусами атомов компонентов сплава, приведенными в обобщенной периодической системе элементов. Показано, что расчет Ms(min) согласуется с экспериментальными данными для чистого железа и сплавов FeNi, FeC.